  1.罐体坯料
  1. Can body blank
  高强度状态(超硬状态)合金3004用于制造罐体。为了获得更佳的强度和拉拔特性的结合,铝板生产厂家需要对钢锭的均质化、热轧、中间退火和冷轧进行严格的控制。
  Alloy 3004 in high strength state (super hard state) is used to make tank body. In order to obtain the best combination of strength and drawing characteristics, aluminum plate manufacturers need to strictly control the homogenization, hot rolling, intermediate annealing and cold rolling of ingots.

铝板生产厂家
  薄板退火后抗拉强度降低。采用连续退火工艺(CAL -IA工艺)处理的板材在连续退火线上的抗拉强度比间歇式炉分批-IA工艺处理的板材的抗拉强度高10mpa,如表1所示。
  The tensile strength of the sheet decreases after annealing. The tensile strength of the continuous annealing process (cal-ia process) treated plate on the continuous annealing line is 10MPa higher than that of the batch furnace ia process treated plate, as shown in Table 1.
  2.罐盖坯料
  2. Tank cover blank
  合金5182-hi8和合金5082-h18分别用于制作啤酒罐或碳酸饮料罐的盖子和接头。装饮料时,饮料罐内含有气压。5052—Hi8合金角用于制造无气压的果汁饮料罐头。
  Alloy 5182-hi8 and alloy 5082-h18 are respectively used to make caps and joints of beer cans or soda cans. When filling drinks, the cans contain air pressure. 5052-hi8 alloy angle is used to make juice beverage cans without air pressure.
  在生产各向异性低、强度高、成形性好的罐盖毛坯时,应特别注意热轧、中间退火和冷轧条件的组合的选择。
  In the production of tank cover blanks with low anisotropy, high strength and good formability, special attention should be paid to the combination of hot rolling, intermediate annealing and cold rolling conditions.