氧化膜对花纹铝板的质量有很大的影响。氧化膜是指铝板在生产过程中的厚度、孔隙率、透明度。将铝板的膜层厚度保持在10um以上，孔隙率和透明度都可以，这样可以获得更好的染色质量。
　　The oxide film has a great influence on the quality of patterned aluminum plate. Oxide film refers to the thickness, porosity and transparency of aluminum plate in the production process. Keeping the film thickness of aluminum plate above 10um, porosity and transparency can be achieved, so that better dyeing quality can be obtained.
　　染色温度
　　Dyeing temperature
　　在染色过程中，铝板分为冷染和热染。采用冷染色，所用时间较长，在染色过程中色彩均匀性较好把握。热染色的使用时间相对较短，但在染色过程中很难控制颜色。热染色温度一般为10-60℃。如果在染色过程中温度过高，染色的吸附性就会降低，容易导致铝板表面起毛。

　　In the process of dyeing, aluminum plate can be divided into cold dyeing and hot dyeing. Cold dyeing takes a long time, and the color uniformity is well controlled in the dyeing process. The use time of thermal dyeing is relatively short, but it is difficult to control the color in the dyeing process. The temperature of hot dyeing is generally 10-60 ℃. If the temperature is too high in the dyeing process, the adsorption of dyeing will be reduced, which is easy to cause the surface of aluminum plate to bristle.
　　铝板件原材料的影响
　　The influence of raw materials on aluminum plate在生产过程中，对高纯铝、铝镁和铝锰合金进行阳极氧化，其中着色功能更好，并可染成多种颜色。对于含硅或含铜较重的板材，在染色过程中只能染成深色和黑色，颜色较单调。
　　In the production process, high-purity aluminum, aluminum magnesium and aluminum manganese alloy are anodized, of which the coloring function is the best and can be dyed into many colors. In the process of dyeing, only dark color and black color can be dyed for the heavy plate containing silicon or copper, and the color is monotonous.
　　铝板的浓度与染色有一定的关系。如果将铝板染成浅色，浓度可以降低一点，而染成深色时浓度可以提高一点。
　　There is a certain relationship between the concentration of aluminum and dyeing. If the aluminum plate is dyed light, the concentration can be reduced a little, while when it is dyed dark, the concentration can be increased a little.
　　一般浅染的花纹铝板材料颜色为0.1-0.39g/L，浅染的颜色为1g/L，深染的颜色为3-5g/L，密染的颜色为10-15g/L。如果要求的染色浓度较高，就会出现颜色不平衡或浮色现象，在清洗和封闭的过程中容易产生流动的颜色。
　　Generally, the color of light dyed aluminum plate is 0.1-0.39g/l, light dyed is 1g / L, dark dyed is 3-5g / L, and dense dyed is 10-15g / L. If the required dyeing concentration is high, there will be color imbalance or floating phenomenon, which is easy to produce flowing color in the process of cleaning and sealing.
　　为了提高染色的吸附性能，可以采用低浓度的染料进行延伸染色，使染料更均匀地渗透到氧化膜中，使染色更加和谐牢固。
　　In order to improve the adsorption property of dyeing, low concentration dye can be used to extend dyeing, so that the dye can penetrate into the oxide film more evenly, making the dyeing more harmonious and firm.
　　以上是铝板生产厂家为大家介绍的相关内容，想要了解更多内容，欢迎访问网站：http://www.jndclyyxgs.comThe above is the relevant content introduced by the aluminum plate manufacturer for you. To learn more, please visit the website: http://www.jndclyxgs.com