As the most commonly used two types, 3003 and 5052 aluminium plates, what's the difference between them? I believe many of you do not know the difference between them, so let Jinan Decheng Aluminum Co., Ltd. Xiaobian take 3003h24 and 5052h24 as examples to popularize this knowledge for you.
Firstly, in terms of chemical composition, 3003 belongs to Al-Mn alloy, and the main alloy element is manganese. 5052 belongs to Al-Mg alloy, the main alloying element is magnesium. In addition, the aluminium content of 3003 is slightly higher than that of 5052 aluminium sheet.
其次，在力学性能方面，3003H24铝板的抗拉强度为145-195rm /MPa，而5052H24铝板的抗拉强度为230-280rm /MPa，远远高于3003H24铝板。3003H24铝板的拉伸强度为115Rm/MPa, 5052H24铝板的拉伸强度为150Rm/MPa。因此，5052铝板的性能明显优于3003铝板。
Secondly, in terms of mechanical properties, the tensile strength of 3003H24 aluminium sheet is 145-195rm/MPa, while that of 5052H24 aluminium sheet is 230-280rm/MPa, which is much higher than that of 3003H24 aluminium sheet. The tensile strength of 3003H24 aluminium sheet is 115Rm/MPa and 5052H24 aluminium sheet is 150Rm/MPa. Therefore, the performance of 5052 aluminium sheet is obviously better than that of 3003 aluminium sheet.
Thirdly, in terms of specifications, 3003 aluminium sheet is mainly made of thin sheet, and the application of thick sheet is basically less. The 5052 aluminium plate is not only used for large sheets, but also for very large thick sheets.
Fourth, in terms of price, the price of 3003 aluminium sheet is slightly higher than that of pure aluminium sheet. The price of 5052 aluminium sheet is obviously higher than that of 3003 aluminium sheet. According to the thickness and specifications, under the same circumstances, the price of 5052 aluminium sheet is about 2,000 yuan higher than that of 3003 aluminium sheet.
Do you know the difference between 3003 and 5052 aluminium sheets? If you still don't understand anything, you can contact Xiaobian, Xiaobian will answer for you at any time. Source: Aluminum coil manufacturer http://www.jndclyyxgs.com