Different industries and categories have different functional requirements for aluminium sheets. In mechanical processing and other industries, the hardness requirements for aluminium sheets are particularly stringent, which requires hardening treatment in the production process of aluminium sheets to improve the hardness of aluminium sheets and meet the functional requirements.
At present, there are two main processing methods: processing strengthening and solution strengthening. The following two methods are briefly introduced in Hangzhou Aluminum Wholesale:
1. Processing strengthened aluminium sheet
Processing strengthening, also known as cold work hardening, is the cold deformation of aluminum sheet under recrystallization temperature, such as casting, calendering, drawing and drawing. When cold deformation occurs, the dislocation density inside the aluminum sheet increases, and intertwines with each other to form cellular structure to prevent dislocation movement.
The larger the deformation degree, the more severe the dislocation entanglement, the greater the deformation resistance and the higher the strength. The degree of strengthening after cold deformation varies with the degree of deformation, the temperature of deformation and the properties of the material itself. When the same material is cold deformed at the same temperature, the greater the deformation degree, the higher the strength and the lower the plasticity.
2. Solution strengthened aluminium sheet
Adding some alloying elements to pure aluminium to form infinite solid solution or finite solid solution can not only obtain high strength, but also obtain excellent plasticity and good pressure processing function.
Copper, magnesium, manganese, zinc, silicon and nickel are the most commonly used alloying elements in solution strengthening of general aluminium sheets. Generally, the alloying of aluminium sheets constitutes a limited solid solution, such as Al-Cu, Al-Mg, Al-Zn, Al-Si, Al-Mn binary alloys, which constitute a limited solid solution, and have a greater limit solubility to play a greater solid solution strengthening effect.
The hardness function of the strengthened aluminium sheet will be significantly improved, but its hardness can not always be improved; when the upper limit of hardness is reached, no matter what method, it can not continue to improve the hardness of the aluminium sheet, only the brand with higher basic hardness can be selected.
The above information is published by our aluminium plate manufacturer. We hope you can help us with our website: http://www.jndclyyxgs.com!