6061铝板的凸显出来哪些优势特点?

来源:http://www.jndclyyxgs.com/ 发布时间:2018-02-05

从生产过程来看,6061合金从半连续铸锭、均匀化、锯切、铣面、包铝、加热、热轧、退火、冷轧、退火、冷轧、固溶处理、时效处理,到剪切、矫平、检验、涂油包装的这一系列的工艺流程,构成了6061合金生产的完整步骤。
From the production process, from the 6061 alloy semi continuous casting, homogenization, sawing, milling, aluminum, heating, hot rolling, cold rolling, cold rolling, annealing, annealing, solid solution treatment, aging treatment, to cut, straightening, inspection, oiling and packaging of this series of process, constitute a complete procedure 6061 alloy production.
6061铝板的生产工艺已非常成熟目前,目前,国内从事6061合金生产的厂家就有数十家,而河南明泰铝业就是其中一个具有代表性的领军企业。
6061, the production technology of aluminum plate has been very mature. At present, there are ten domestic enterprises engaged in the production of 6061 alloys, and Henan Ming Tai aluminum industry is one of the representative leading enterprises.
6061铝板是6系的重要产品,因此,明泰铝业设置了精准的生产控制,严格的质量检测,来保证产品的工艺成熟,性能优越。例如,在进行质量检测时,就对6061铝板三个关键指标进行了精准检测。一是组织细小、性能均匀。
6061 aluminum plate is an important product of the 6 department. Therefore, Ming Tai aluminum has set up precise production control and strict quality inspection to ensure that the product's technology is mature and its performance is superior. For example, in quality testing, three key indicators of 6061 aluminum plates are accurately tested. One is small tissue and uniform performance.
特别是对于超厚板,要求厚度方向上的性能均匀,不能有较大的性能波动,对于中厚板、薄板,在长度、宽度上同样不能存在较大性能波动;二是尺寸精度较高。主要包括厚度精准和宽度精准,尤其是难度较大要求很严的厚度精度,将直接影响到使用性能和后续加工;三是板形良好。板形包括平直度和板凸度。因为二者对后续加工有很大影响,并且不可逆。

铝板生产厂家
Especially for super thick plate, the thickness direction performance is uniform, and there is no greater performance fluctuation. For medium plate and thin plate, there is no big performance fluctuation in length and width, and the two is high dimensional accuracy. It mainly includes thickness accuracy and width accuracy, especially the thickness accuracy which is most difficult and strict. It will directly affect the performance and subsequent processing. Three, the shape is good. The shape of the plate consists of flatness and plate convexity. Because the two have a great impact on the subsequent processing, and irreversible.
6061铝合金常用状态有T6和T651,一般情况下,T6的内应力会比较大,加工会变形。因此,较适合加工的状态是T651,T651状态是在T6的基础上进行拉伸,消除内应力,是经过热处理预拉伸工艺的高品质铝合金产品。
6061 aluminum alloys are commonly used in the state of T6 and T651. In general, the internal stress of T6 will be larger and the processing will be deformed. Therefore, the most suitable state for processing is T651. T651 state is stretched on the basis of T6 to eliminate internal stress. It is a high quality aluminum alloy product after heat treatment and pre stretching process.
6061-T651铝板强度不能与2系、7系合金产品相比,但是,由于其镁硅元素存在,因此,6061铝板具备的焊接性、耐蚀性和冷加工性,可阳极氧化着色,也可进行涂漆,是一种使用范围广泛的合金,在建筑装饰领域也常常使用。
6061-T651 aluminum plate and 2 line, 7 strength alloy products compared, however, due to the presence of the magnesium silicon, therefore, 6061 aluminum has excellent weldability, corrosion resistance and cold workability, anodizing can also be painted, is a kind of alloy widely used, are often used in building decoration field.
铝板在生产过程中,因为受热和挤压,造成晶体间密度不均匀,能量得不到完全释放,积蓄在铝板内部,这个能量称为内应力。某些用户的生产工艺(如加温、折弯、深冲、拉伸等)会释放出铝板的内应力,造成铝板弯曲、波浪纹、表面不平等,所以需要先释放出铝板的内应力。
Aluminum plate in the production process, because of heat and extrusion, resulting in uneven density between crystals, energy can not be fully released, accumulated in the aluminum plate, this energy is called internal stress. Some users' production processes (such as heating, bending, deep drawing, stretching, etc.) will release the internal stress of aluminum plates, causing the bending, waviness and surface inequalities of aluminum plates, so we need to release the internal stress of aluminum plates first.
以上就是为大家介绍的有关铝板生产厂家http://www.jndclyyxgs.com的详细的介绍,希望对您有所帮助.如果您有什么疑问的话,欢迎联系我们.我们将以较的态度,为您提供服务.
The above is a detailed introduction to http://www.jndclyyxgs.com about aluminum plate manufacturer, I hope to help you. If you have any questions, please feel free to contact us. We will provide you with the most professional attitude.